This bath is characterised by firmly adhering, hard and tarnish-resistant gold deposits.
In addition to conventional metallisable materials, the bath is also suitable for stainless steels.
The strongly acidic bath also has a stronger activation capacity.

Processing is used in conventional electroplating systems. If necessary, the pH value is adjusted with diluted sulphuric acid.

A degreased surface is a prerequisite.

Data:

• 
  
• Gold content** (g/l): 3.0
  
• Temperature (°C): 20 - 30
  
• Exposure time (min): 10 - 25
  
• Voltage (volts): 3.0 - 4.0
  
• Current density (A/dm²): 0.5 - 1.2
  
• Deposition (mg/Amin): 16
  
• pH value: 1.5 - 1.8
  
• Movement of electrolyte or fabric
  
• Anodes: Titanium, platinised
  
• Tub material: Glass, acid-resistant plastic Plastic
  
• Density (g/cm³): 18.2
  
• Hardness (HV): 110
  
• Layer thickness (µm): < 6
  

Delivery form: ready to use
Content (litre): 1
Regeneration: add required amount of regeneration concentrate after analysis
Dangerous goods: YES

** The precious metal content is calculated at the current daily rate!